Řada VSM17

Workpiece Material

PP Steel (12)
- P0P0
  Low-Carbon Steels, Long Chipping C < .25%; <125 HB; <530 N/mm^2 UTS(12)
- P1P1
  Low-Carbon Steels, Short Chipping C < .25%; <125 HB; <530 N/mm^2 UTS(12)
- P2P2
  Medium and High Carbon Steels C < .25%; <220 HB; <25 HRC; >530 N/mm^2 UTS(12)
- P3P3
  Alloy Steels & Tool Steels C > .25%; <330 HB; <35 HRC; 600-850 N/mm^2 UTS(12)
- P4P4
  Alloy Steels & Tool Steels C > .25%; 350-420 HB; 35-43 HRC; 850-1400 N/mm^2 UTS(12)
- P5P5
  Ferritic, Martensitic, and PH Stainless Steels <330 HB; <35 HRC; 600-900 N/mm^2 UTS(12)
- P6P6
  High Strength Ferritic, Martensitic, and PH Stainless Steels 350-450 HB; 35-43 HRC; 900-2400 N/mm^2 UTS(12)
MM Stainless Steel (12)
- M1M1
  Austenitic Stainless Steel 130-200 HB; <600 N/mm^2 UTS(12)
- M2M2
  High Strength Austenitic Stainless and Cast Stainless Steels 150-230 HB; <25 HRC; >600 N/mm^2 UTS(12)
- M3M3
  Duplex Stainless Steel 135-275 HB; <30 HRC; 500-1200 N/mm^2 UTS(12)
KK Cast Iron (12)
- K1K1
  Gray Cast Iron 120-290 HB; <32 HRC; 125-500 N/mm^2 UTS(12)
- K2K2
  Low and Medium Strength CGI and Ductile Irons 130-260 HB; <28 HRC; <600 N/mm^2 UTS(12)
- K3K3
  High Strength Ductile and Austempered Ductile Iron 180-350 HB; <43 HRC; >600 N/mm^2 UTS(12)
NN Non-Ferrous Materials (12)
- N1N1
  Wrought Aluminum (12)
- N2N2
  Low-Silicon Aluminum Alloys and Magnesium Alloys Si <12.2%(12)
- N3N3
  High-Silicon Aluminum Alloys Si >12.2%(12)
SS High-Temp Alloys (12)
- S1S1
  Iron-Based, Heat-Resistant Alloys 160-260 HB; 25-48 HRC; 500-1200 N/mm^2 UTS(12)
- S2S2
  Cobalt-Based, Heat-Resistant Alloys 250-450 HB; 25-48 HRC; 1000-1450 N/mm^2 UTS(12)
- S3S3
  Nickel-Based, Heat Resistant Alloys 160-450 HB; <48 HRC; 600-1700 N/mm^2 UTS(12)
- S4S4
  Titanium and Titanium Alloys 300-400 HB; 33-43 HRC; 900-1600 N/mm^2 UTS(12)
HH Hardened Materials (12)
- H1H1
  Hardened Materials 44-48 HRC(12)