| Номер материала | 3563900 |
| Идентификатор каталога ISO | HNGJ0905ANSNHD |
| Идентификатор каталога ANSI | HNGJ535ANSNHD |
| Grade | TN6520 |
| Cutting Edges per Insert | 12 |
| [D] Insert IC Size | 15.875 mm |
| [D] Insert IC Size | .625 in |
| [L10] Insert Cutting Edge Length | 8.593 mm |
| [L10] Insert Cutting Edge Length | .3383 in |
| [S] Insert Thickness | 5.463 mm |
| [S] Insert Thickness | .2151 in |
| [BS] Corner Facet Length | 1.653 mm |
| [BS] Corner Facet Length | .0651 in |
| [Rε] Corner Radius | 1.2 mm |
| [Rε] Corner Radius | .0468 in |
| Average Chip Thickness [HM] | 0.17 mm |
| Average Chip Thickness [HM] | .0069 in |
Создать решение для расчета подачи и скорости
После создания решения просто выберите значок Подача и Скорость, и наша система предоставит рекомендации. Вы можете настроить информацию, добавив свою машину и характеристики или внести изменения с помощью слайдеров.
| Material Group | Light | General | Heavy | Universal | ||||
| Geometry | Grade | Geometry | Grade | Geometry | Grade | Geometry | Grade | |
| P1–P2 | .E..LD | WP40PM | .S..GD | WP40PM | .S..HD | WP40PM | .S..MM | WU20PM |
| P3–P4 | .E..LD | WP25PM | .S..GD | WP35CM | .S..HD | WP35CM | .S..MM | WU20PM |
| P5–P6 | .E..LD | WP25PM | .S..GD | WP35CM | .S..HD | WP35CM | .S..MM | WP35CM |
| M1–M2 | .E..LD | WP25PM | .S..GD | WP25PM | .S..HD | WP25PM | .S..MM | WU20PM |
| M3 | .E..LD | WP35CM | .S..GD | WP35CM | .S..HD | WP35CM | .S..MM | WP35CM |
| K1–K2 | .E..LD | TN6520 | .S..GD | WK15CM | .S..HD | WK15CM | .S..MM | WK15CM |
| K3 | .E..LD | WP35CM | .S..GD | WP35CM | .S..HD | WP35CM | .S..MM | WP35CM |
| N1–N2 | .F..LDJ | TN6501 | .F..LDJ | TN6501 | .F..LDJ | TN6501 | ||
| N3 | .F..LDJ | TN6501 | .F..LDJ | TN6501 | .F..LDJ | TN6501 | ||
| S1–S2 | .E..LD | WS30PM | .S..GD | WS30PM | .S..HD | WS40PM | .S..MM | WU20PM |
| S3 | .E..LD | WS30PM | .S..GD | WS30PM | .S..HD | WS40PM | .S..MM | WU20PM |
| S4 | .E..LD | WS30PM | .S..GD | WS30PM | .S..HD | WS40PM | .S..MM | WU20PM |
| Light | General | Heavy |
| M1200 15º Lead • Recommended Starting Feeds [mm/th] | ||||||
| Insert Geometry | Programmed Feed per Tooth (fz) at a % of Radial Depth of Cut (ae) | |||||
| 30% | 40 | |||||
| L | M | H | L | M | H | |
| .F..LDJ | 0,22 | 0,42 | 0,83 | 0,21 | 0,38 | 0,76 |
| .E..LD | 0,22 | 0,64 | 1,28 | 0,21 | 0,59 | 1,17 |
| .S..GD | 0,43 | 1,07 | 1,72 | 0,39 | 0,98 | 1,57 |
| .S..HD | 0,43 | 1,07 | 1,72 | 0,39 | 0,98 | 1,57 |
| .S..Ceramic | – | – | – | – | – | – |
| .S..MM | 0,43 | 1,07 | 1,72 | 0,39 | 0,98 | 1,57 |
| L = Light Machining; M = Medium Machining; H = Heavy Machining NOTE: Use "Light Machining" values as starting feed rate. | ||||||
| Light | General | Heavy |
| M1200 15º Lead • Recommended Starting Feeds [IPT] | ||||||
| Insert Geometry | Programmed Feed per Tooth (fz) at a % of Radial Depth of Cut (ae) | |||||
| 30% | 40 | |||||
| L | M | H | L | M | H | |
| .F..LDJ | 0.008 | 0.017 | 0.034 | 0.008 | 0.015 | 0.031 |
| .E..LD | 0.008 | 0.025 | 0.051 | 0.008 | 0.023 | 0.046 |
| .S..GD | 0.017 | 0.042 | 0.068 | 0.015 | 0.039 | 0.062 |
| .S..HD | 0.017 | 0.042 | 0.068 | 0.015 | 0.039 | 0.062 |
| .S..Ceramic | – | – | – | – | – | – |
| .S..MM | 0.017 | 0.042 | 0.068 | 0.015 | 0.039 | 0.062 |
| L = Light Machining; M = Medium Machining; H = Heavy Machining NOTE: Use "Light Machining" values as starting feed rate. | ||||||
| M1200 • Recommended Starting Speeds [m/min] | ||||||||||||||||||||||
| Grade | THM-U | TN6501 | TN6510 | TN6520 | TN6525 | TN6540 | WK15CM | |||||||||||||||
| Chip Thickness hex mm | Min | Max | Min | Max | Min | Max | Min | Max | Min | Max | Min | Max | Min | Max | ||||||||
| Material Group | Max | Start | Min | Max | Start | Min | Max | Start | Min | Max | Start | Min | Max | Start | Min | Max | Start | Min | Max | Start | Min | |
| P | 1 | – | – | – | – | – | – | – | – | – | – | – | – | 410 | 320 | 280 | 360 | 280 | 240 | – | – | – |
| 2 | – | – | – | – | – | – | – | – | – | – | – | – | 320 | 250 | 215 | 250 | 190 | 170 | – | – | – | |
| 3 | – | – | – | – | – | – | – | – | – | – | – | – | 280 | 215 | 185 | 215 | 170 | 140 | – | – | – | |
| 4 | – | – | – | – | – | – | – | – | – | – | – | – | 235 | 170 | 145 | 180 | 130 | 110 | – | – | – | |
| 5 | – | – | – | – | – | – | – | – | – | – | – | – | 310 | 235 | 200 | 240 | 180 | 150 | – | – | – | |
| 6 | – | – | – | – | – | – | – | – | – | – | – | – | 205 | 160 | 130 | 160 | 120 | 100 | – | – | – | |
| M | 1 | – | – | – | – | – | – | – | – | – | – | – | – | 190 | 120 | 80 | 130 | 80 | 60 | – | – | – |
| 2 | – | – | – | – | – | – | – | – | – | – | – | – | 120 | 80 | 50 | 80 | 50 | 40 | – | – | – | |
| 3 | – | – | – | – | – | – | – | – | – | – | – | – | 125 | 80 | 55 | 85 | 50 | 40 | – | – | – | |
| K | 1 | – | – | – | – | – | – | 480 | 350 | 260 | 450 | 320 | 230 | 275 | 245 | 220 | 220 | 205 | 180 | 505 | 460 | 410 |
| 2 | – | – | – | – | – | – | 420 | 280 | 205 | 390 | 250 | 190 | 215 | 190 | 180 | 175 | 155 | 140 | 400 | 355 | 330 | |
| 3 | – | – | – | – | – | – | 335 | 260 | 200 | 300 | 230 | 160 | 180 | 160 | 145 | 155 | 145 | 125 | 335 | 300 | 275 | |
| N | 1 | 2400 | 1440 | 1200 | 2400 | 1440 | 1200 | – | – | – | – | – | – | – | – | – | – | – | – | – | – | – |
| 2 | 1640 | 980 | 800 | 1640 | 980 | 800 | – | – | – | – | – | – | – | – | – | – | – | – | – | – | – | |
| 3 | 960 | 600 | 480 | 960 | 600 | 480 | – | – | – | – | – | – | – | – | – | – | – | – | – | – | – | |
| S | 1 | – | – | – | – | – | – | – | – | – | – | – | – | – | – | – | 50 | 35 | 30 | – | – | – |
| 2 | – | – | – | – | – | – | – | – | – | – | – | – | – | – | – | 25 | 20 | 10 | – | – | – | |
| 3 | – | – | – | – | – | – | – | – | – | – | – | – | – | – | – | 70 | 40 | 30 | – | – | – | |
| 4 | – | – | – | – | – | – | – | – | – | – | – | – | – | – | – | 60 | 30 | 25 | – | – | – | |
| H | 1 | – | – | – | – | – | – | – | – | – | – | – | – | – | – | – | – | – | – | – | – | – |
| Recommended Starting Speed are pointing to 90° Shoulder Milling . Starting Speed for Face and Copy Milling can be Increased by 20 %. As the average chip thickness increases, speed should be decreased. Material groups P, M, K and H show recommended starting speeds for dry machining. For wet machining, reduce speed by 20%. Material groups N and S show recommended starting speeds for wet machining. Not recommended for dry machining. | ||||||||||||||||||||||
| M1200 • Recommended Starting Speeds [m/min] | ||||||||||||||||||||||
| Grade | WP25PM | WP35CM | WP40PM | WS30PM | WS40PM | WU20PM | WK25YM | |||||||||||||||
| Chip Thickness hex mm | Min | Max | Min | Max | Min | Max | Min | Max | Min | Max | Min | Max | Min | Max | ||||||||
| Material Group | Max | Start | Min | Max | Start | Min | Max | Start | Min | Max | Start | Min | Max | Start | Min | Max | Start | Min | Max | Start | Min | |
| P | 1 | 395 | 340 | 325 | 545 | 475 | 445 | 355 | 310 | 295 | – | – | – | – | – | – | 330 | 290 | 270 | – | – | – |
| 2 | 330 | 290 | 240 | 335 | 305 | 275 | 300 | 260 | 215 | – | – | – | – | – | – | 275 | 250 | 200 | – | – | – | |
| 3 | 305 | 260 | 210 | 305 | 275 | 245 | 275 | 235 | 190 | – | – | – | – | – | – | 255 | 220 | 175 | – | – | – | |
| 4 | 270 | 220 | 180 | 230 | 210 | 190 | 245 | 205 | 160 | – | – | – | – | – | – | 225 | 190 | 150 | – | – | – | |
| 5 | 220 | 205 | 180 | 310 | 275 | 250 | 205 | 185 | 160 | – | – | – | 205 | 175 | 145 | 185 | 175 | 150 | – | – | – | |
| 6 | 200 | 150 | 120 | 190 | 160 | 130 | 180 | 140 | 110 | – | – | – | 180 | 130 | 95 | 165 | 130 | 100 | – | – | – | |
| M | 1 | 245 | 215 | 200 | 245 | 220 | 185 | 235 | 205 | 185 | 270 | 240 | 220 | 250 | 205 | 170 | 205 | 180 | 165 | – | – | – |
| 2 | 220 | 190 | 155 | 220 | 190 | 170 | 210 | 180 | 150 | 245 | 215 | 175 | 215 | 175 | 145 | 185 | 160 | 130 | – | – | – | |
| 3 | 170 | 145 | 115 | 175 | 155 | 140 | 155 | 140 | 110 | 185 | 160 | 125 | 175 | 130 | 100 | 140 | 120 | 95 | – | – | – | |
| K | 1 | 275 | 245 | 220 | 355 | 320 | 290 | – | – | – | – | – | – | – | – | – | 250 | 220 | 185 | 965 | 880 | 780 |
| 2 | 215 | 190 | 180 | 280 | 250 | 230 | – | – | – | – | – | – | – | – | – | 200 | 180 | 150 | 765 | 685 | 635 | |
| 3 | 180 | 160 | 145 | 235 | 210 | 190 | – | – | – | – | – | – | – | – | – | 180 | 150 | 120 | 645 | 570 | 525 | |
| N | 1 | – | – | – | – | – | – | – | – | – | – | – | – | – | – | – | 550 | 470 | 400 | – | – | – |
| 2 | – | – | – | – | – | – | – | – | – | – | – | – | – | – | – | 550 | 470 | 400 | – | – | – | |
| 3 | – | – | – | – | – | – | – | – | – | – | – | – | – | – | – | 400 | 350 | 300 | – | – | – | |
| S | 1 | 50 | 40 | 30 | – | – | – | 50 | 40 | 35 | 55 | 50 | 35 | 50 | 40 | 30 | 40 | 35 | 25 | – | – | – |
| 2 | 50 | 40 | 30 | – | – | – | 50 | 40 | 35 | 55 | 50 | 35 | 50 | 40 | 30 | 40 | 35 | 25 | – | – | – | |
| 3 | 60 | 50 | 30 | – | – | – | 60 | 50 | 35 | 65 | 55 | 35 | 60 | 50 | 30 | 50 | 40 | 25 | – | – | – | |
| 4 | 85 | 60 | 40 | 80 | 60 | 40 | 80 | 60 | 40 | 100 | 70 | 50 | 70 | 60 | 35 | 70 | 50 | 35 | – | – | – | |
| H | 1 | 145 | 110 | 85 | – | – | – | – | – | – | – | – | – | – | – | – | 110 | 80 | 70 | – | – | – |
| Recommended Starting Speed are pointing to 90° Shoulder Milling . Starting Speed for Face and Copy Milling can be Increased by 20 %. As the average chip thickness increases, speed should be decreased. Material groups P, M, K and H show recommended starting speeds for dry machining. For wet machining, reduce speed by 20%. Material groups N and S show recommended starting speeds for wet machining. Not recommended for dry machining. | ||||||||||||||||||||||
| M1200 • Recommended Starting Speeds [SFM] | ||||||||||||||||||||||
| Grade | THM-U | TN6501 | TN6510 | TN6520 | TN6525 | TN6540 | WK15CM | |||||||||||||||
| Chip Thickness hex Inch | Min | Max | Min | Max | Min | Max | Min | Max | Min | Max | Min | Max | Min | Max | ||||||||
| Material Group | Max | Start | Min | Max | Start | Min | Max | Start | Min | Max | Start | Min | Max | Start | Min | Max | Start | Min | Max | Start | Min | |
| P | 1 | – | – | – | – | – | – | – | – | – | – | – | – | 1340 | 1045 | 925 | 1180 | 925 | 785 | – | – | – |
| 2 | – | – | – | – | – | – | – | – | – | – | – | – | 1045 | 830 | 710 | 830 | 630 | 550 | – | – | – | |
| 3 | – | – | – | – | – | – | – | – | – | – | – | – | 925 | 710 | 610 | 710 | 550 | 450 | – | – | – | |
| 4 | – | – | – | – | – | – | – | – | – | – | – | – | 770 | 550 | 475 | 590 | 430 | 355 | – | – | – | |
| 5 | – | – | – | – | – | – | – | – | – | – | – | – | 1025 | 770 | 650 | 785 | 590 | 490 | – | – | – | |
| 6 | – | – | – | – | – | – | – | – | – | – | – | – | 670 | 535 | 430 | 535 | 395 | 335 | – | – | – | |
| M | 1 | – | – | – | – | – | – | – | – | – | – | – | – | 630 | 395 | 260 | 430 | 260 | 200 | – | – | – |
| 2 | – | – | – | – | – | – | – | – | – | – | – | – | 395 | 260 | 155 | 260 | 155 | 140 | – | – | – | |
| 3 | – | – | – | – | – | – | – | – | – | – | – | – | 415 | 260 | 180 | 275 | 155 | 140 | – | – | – | |
| K | 1 | – | – | – | – | – | – | 1570 | 1140 | 845 | 1475 | 1045 | 750 | 905 | 805 | 725 | 725 | 670 | 590 | 1655 | 1520 | 1340 |
| 2 | – | – | – | – | – | – | 1380 | 925 | 670 | 1280 | 830 | 630 | 710 | 630 | 590 | 570 | 510 | 450 | 1320 | 1165 | 1080 | |
| 3 | – | – | – | – | – | – | 1105 | 845 | 650 | 985 | 750 | 535 | 590 | 535 | 475 | 510 | 475 | 415 | 1105 | 985 | 905 | |
| N | 1 | 7870 | 4720 | 3935 | 7870 | 4720 | 3935 | – | – | – | – | – | – | – | – | – | – | – | – | – | – | – |
| 2 | 5370 | 3210 | 2615 | 5370 | 3210 | 2615 | – | – | – | – | – | – | – | – | – | – | – | – | – | – | – | |
| 3 | 3150 | 1970 | 1570 | 3150 | 1970 | 1570 | – | – | – | – | – | – | – | – | – | – | – | – | – | – | – | |
| S | 1 | – | – | – | – | – | – | – | – | – | – | – | – | – | – | – | 155 | 120 | 95 | – | – | – |
| 2 | – | – | – | – | – | – | – | – | – | – | – | – | – | – | – | 80 | 60 | 40 | – | – | – | |
| 3 | – | – | – | – | – | – | – | – | – | – | – | – | – | – | – | 235 | 140 | 95 | – | – | – | |
| 4 | – | – | – | – | – | – | – | – | – | – | – | – | – | – | – | 200 | 95 | 80 | – | – | – | |
| H | 1 | – | – | – | – | – | – | – | – | – | – | – | – | – | – | – | – | – | – | – | – | – |
| Recommended Starting Speed are pointing to 90° Shoulder Milling . Starting Speed for Face and Copy Milling can be Increased by 20 %. As the average chip thickness increases, speed should be decreased. Material groups P, M, K and H show recommended starting speeds for dry machining. For wet machining, reduce speed by 20%. Material groups N and S show recommended starting speeds for wet machining. Not recommended for dry machining. | ||||||||||||||||||||||
| M1200 • Recommended Starting Speeds [SFM] | ||||||||||||||||||||||
| Grade | WP25PM | WP35CM | WP40PM | WS30PM | WS40PM | WU20PM | WK25YM | |||||||||||||||
| Chip Thickness hex Inch | Min | Max | Min | Max | Min | Max | Min | Max | Min | Max | Min | Max | Min | Max | ||||||||
| Material Group | Max | Start | Min | Max | Start | Min | Max | Start | Min | Max | Start | Min | Max | Start | Min | Max | Start | Min | Max | Start | Min | |
| P | 1 | 1295 | 1120 | 1060 | 1790 | 1555 | 1460 | 970 | 855 | 805 | – | – | – | – | – | – | 1080 | 950 | 890 | – | – | – |
| 2 | 1080 | 940 | 785 | 1105 | 1000 | 905 | 820 | 705 | 590 | – | – | – | – | – | – | 900 | 820 | 660 | – | – | – | |
| 3 | 1000 | 845 | 690 | 1000 | 905 | 805 | 755 | 640 | 525 | – | – | – | – | – | – | 840 | 720 | 570 | – | – | – | |
| 4 | 890 | 725 | 590 | 750 | 690 | 630 | 675 | 560 | 445 | – | – | – | – | – | – | 740 | 620 | 490 | – | – | – | |
| 5 | 725 | 670 | 590 | 1025 | 905 | 830 | 560 | 510 | 445 | – | – | – | 560 | 475 | 395 | 610 | 570 | 490 | – | – | – | |
| 6 | 650 | 490 | 395 | 630 | 535 | 430 | 490 | 375 | 295 | – | – | – | 490 | 360 | 260 | 540 | 430 | 330 | – | – | – | |
| M | 1 | 805 | 710 | 650 | 805 | 725 | 610 | 640 | 560 | 510 | 890 | 785 | 725 | 690 | 560 | 460 | 670 | 590 | 540 | – | – | – |
| 2 | 725 | 630 | 510 | 725 | 630 | 550 | 575 | 490 | 410 | 805 | 710 | 570 | 590 | 475 | 395 | 610 | 520 | 430 | – | – | – | |
| 3 | 550 | 475 | 370 | 570 | 510 | 450 | 425 | 375 | 295 | 610 | 535 | 415 | 475 | 360 | 280 | 460 | 390 | 310 | – | – | – | |
| K | 1 | 905 | 805 | 725 | 1165 | 1045 | 940 | – | – | – | – | – | – | – | – | – | 820 | 720 | 610 | 3170 | 2880 | 2560 |
| 2 | 710 | 630 | 590 | 925 | 830 | 750 | – | – | – | – | – | – | – | – | – | 660 | 590 | 490 | 2510 | 2240 | 2090 | |
| 3 | 590 | 535 | 475 | 770 | 690 | 630 | – | – | – | – | – | – | – | – | – | 590 | 490 | 390 | 2110 | 1870 | 1720 | |
| N | 1 | – | – | – | – | – | – | – | – | – | – | – | – | – | – | – | 1800 | 1540 | 1310 | – | – | – |
| 2 | – | – | – | – | – | – | – | – | – | – | – | – | – | – | – | 1800 | 1540 | 1310 | – | – | – | |
| 3 | – | – | – | – | – | – | – | – | – | – | – | – | – | – | – | 1310 | 1150 | 980 | – | – | – | |
| S | 1 | 155 | 140 | 95 | – | – | – | – | – | – | 180 | 155 | 120 | 130 | 115 | 80 | 130 | 110 | 80 | – | – | – |
| 2 | 155 | 140 | 95 | – | – | – | – | – | – | 180 | 155 | 120 | 130 | 115 | 80 | 130 | 110 | 80 | – | – | – | |
| 3 | 200 | 155 | 95 | – | – | – | – | – | – | 215 | 180 | 120 | 165 | 130 | 80 | 160 | 130 | 80 | – | – | – | |
| 4 | 275 | 200 | 140 | 260 | 200 | 130 | – | – | – | 335 | 235 | 155 | 195 | 165 | 100 | 230 | 160 | 110 | – | – | – | |
| H | 1 | 475 | 355 | 275 | – | – | – | – | – | – | – | – | – | – | – | – | 360 | 260 | 230 | – | – | – |
| Recommended Starting Speed are pointing to 90° Shoulder Milling . Starting Speed for Face and Copy Milling can be Increased by 20 %. As the average chip thickness increases, speed should be decreased. Material groups P, M, K and H show recommended starting speeds for dry machining. For wet machining, reduce speed by 20%. Material groups N and S show recommended starting speeds for wet machining. Not recommended for dry machining. | ||||||||||||||||||||||
CAD Drawings Models
Can’t find the file type you’re looking for?
Product data
I have read and accepted the Terms & Conditions of use
Номер по каталогу ISO
Номер по каталогу ANSI
to find similar products.Please select a file to download
Models
. Please enter the desired qty for the material(s) you want to include in your promotion or Proceed Without Promotion and only your base materials will be added to the cart.
Minimum quantity should be
| SAP Material Number | Номер по каталогу ISO | Сплав |
|---|