Kendex™ Negative

Workpiece Material

PP Steel (2)
- P5P5
  Ferritic, Martensitic, and PH Stainless Steels <330 HB; <35 HRC; 600-900 N/mm^2 UTS(2)
- P6P6
  High Strength Ferritic, Martensitic, and PH Stainless Steels 350-450 HB; 35-43 HRC; 900-2400 N/mm^2 UTS(2)
KK Cast Iron (2)
- K1K1
  Gray Cast Iron 120-290 HB; <32 HRC; 125-500 N/mm^2 UTS(2)
- K2K2
  Low and Medium Strength CGI and Ductile Irons 130-260 HB; <28 HRC; <600 N/mm^2 UTS(2)
- K3K3
  High Strength Ductile and Austempered Ductile Iron 180-350 HB; <43 HRC; >600 N/mm^2 UTS(2)
NN Non-Ferrous Materials (2)
- N1N1
  Wrought Aluminum (2)
- N2N2
  Low-Silicon Aluminum Alloys and Magnesium Alloys Si <12.2%(2)
- N4N4
  Copper, Brass, Zinc-based on machinability index range of 70-100 (2)
- N5N5
  Nylon, Plastics, Rubbers, Phenolics, Resins, Fiberglass (2)
- N7N7
  MMC's (2)
SS High-Temp Alloys (2)
- S1S1
  Iron-Based, Heat-Resistant Alloys 160-260 HB; 25-48 HRC; 500-1200 N/mm^2 UTS(2)
- S2S2
  Cobalt-Based, Heat-Resistant Alloys 250-450 HB; 25-48 HRC; 1000-1450 N/mm^2 UTS(2)
- S3S3
  Nickel-Based, Heat Resistant Alloys 160-450 HB; <48 HRC; 600-1700 N/mm^2 UTS(2)
- S4S4
  Titanium and Titanium Alloys 300-400 HB; 33-43 HRC; 900-1600 N/mm^2 UTS(2)
HH Hardened Materials (2)
- H1H1
  Hardened Materials 44-48 HRC(2)
- H2H2
  Hardened Materials 48-55 HRC(2)
- H3H3
  Hardened Materials 56-60 HRC(2)
- H4H4
  Hardened Materials >60 HRC(2)
CC CFRP Materials (2)
- C2C2
  CFRP / Aluminium CFRP / Non-Ferrous (2)